BRASS ROUND (385) 12.00dia
385 Brass - Free Machining
Brass alloy 385 has been specifically developed for the mass production of brass components in high speed lathes, providing maximun output and long tool life.
Typical applications are nuts, bolts and screw thread
COLOUR CODE: red bar end.
BAR FINISH: Cold drawn
HEAT TREATMENT:
ANNEALING: Heat to 425c - 600c, hold until temperature is uniform throughout hte section and cool in furnace
STRESS RELIEVING: Heat to 250c - 300c, hold until temperature is uniform throughout the section
HOT WORKING: Fair hot working properties within an ideal temperature range of 700c to 800c.
COLD WORKING: Exhibits poor cold working properties, and cold heading is not recommended.
MACHINING: A free cutting brass specifically developed for maximum output and longest tool life, ideally suited for mass produced brass components.
CORROSION RESISTANCE: Has good corrosion resistance to weathering, with a fair resistance to many waters. It should not be used in contact with ammonia, or ammonia components, as it may suffer stress corrosion cracking.
PLATING: Provides good surface finish through either polishing, and/or electroplating.
JOINING PROPERTIES:
SOLDERING: - Whilst good results can be achieved from Silver soldering, better results can be achieved from Soft soldering.
BRAZING: - Good results can be achieved from brazing.
WELDING: - Fair results can be achieved from both Oxy acetylene & Carbon arc welding. However Gas shielded and coated metal arc welding, and resistance welding is not recommended.
Weight: 1.000 KG/MTR